PRODUCT NUMBER

PRODUCT NAME

67-20

TILE RED URETHANE ENAMEL

This product is recommended for general maintenance use on masonry and concrete floors, general metal equipment, and wood wherever a good quality alkyd finish is needed. It will provide long term, cost-effective protection against water, salt, oil, alkali cleaners, and household chemicals. Use where the ambient temperature will not exceed 300 ⁰F. Not recommended for immersion service or for areas subject to prolonged chemical solvent exposure.

For best results, metal substrates should be blasted to SSPC-SP-6 commercial blast, with a 1-mil blast profile, and primed with a good quality alkyd primer (such as Pruett-Schaffer #30-12620).Unpainted concrete surfaces should be primed with this material thinned 5-10% with xylol, then recoated within 24 hours with full strength material. All previously painted concrete surfaces should be scraped or sanded to remove all loose coating and to scuff up the surface to provide better adhesion, then washed and allowed to dry completely. Bare wood surfaces should be primed or coated twice with this paint. Existing coatings must be tightly adhering and deglossed by sanding for best adhesion. In general, this coating is very tolerant of less than perfect surface preparation, so hand or power tool cleaning may be sufficient for many applications. At a minimum for acceptable performance, surfaces to be coated must be clean and dry, and free of oil/grease, loose rust/paint, weld spatter, burning slag, dust, and

Under normal conditions no thinning is necessary. Thin with xylol or mineral spirits when using as a primer coat over bare concrete; add a little thinner at a time with constant gentle agitation to a maximum of 10% by volume. If applying to substrates exceeding 90 ⁰F, use Aromatic 100 thinner.

Dries tack free in 2 to 4 hours at 77 ⁰F; dry to light foot traffic or light handling in 18-24 hours; ultimate cure in 7-10 days. If re coating this material with itself, use within 24 hours or intercoat adhesion may be reduced. Force drying ovens may be used, allow 30 minutes minimum for flashoff of solvent before heating.

Clean equipment with mineral spirits, xylol or toluol before the film dries.

This product meets current air pollution regulations regarding hydrocarbon and ozone reactive emissions. It is VOC compliant for the architectural maintenance industry, and contains no lead, chromate, or zinc.

INITIAL GLOSS, 60⁰ , ASTM D-523:

FLASH POINT, TAG CC: 102 ⁰F, as shipped

ANTISAG INDEX, ASTM D-4400: 6 mils

THIS INFORMATION RESULTS FROM TESTS CONDUCTED IN A LABORATORY UNDER LABORATORY CONDITIONS. DIFFERENT RESULTS MAY BE OBTAINED IN COMMERCIAL USE OF THIS PRODUCT UNDER FACTORY OR FIELD CONDITIONS. PRUETT-SCHAFFER MAKES NO WARRANTY CONCERNING THE SUITABILITY OF THIS PRODUCT FOR THE END USE CONTEMPLATED BY THE BUYER, EXCEPT THAT THE PRODUCT SHALL BE IN COMPLIANCE WITH THE TECHNICAL SPECIFICATIONS PRESENTED HEREIN.