www.pruett-schaffer.com

PRODUCT NUMBER	PRODUCT NAME
16-13057-FDA	WHITE FDA EPOXY
GENERAL DESCRIPTION Pruett-Schaffer’s #16-13057 White Epoxy is a two component, polyamide cured epoxy for use where good chemical resistance is needed. It is designed as a high gloss, spray applied, corrosion resistant, heavy duty, topcoat. It exhibits excellent adhesion over a wide variety of substrates, and exceptional corrosion, water and chemical resistance. All components of this product are approved by the FDA for incidental contact with foodstuffs. RECOMMENDED USES Use to protect machinery, tanks, and structures from corrosion in aggressive environments where chemicals, salt, water, fuels, and oils are present. Formulated to allow high film build in one pass to protect hard to cover sharp edges. May also be used as an encapsulation coating. This formula will chalk on long term exposure to sunlight. SURFACE PREPARATION For severe service, metal substrates should be blasted to an SSPC-SP-10 white metal blast with a 1.5 +/- .5 mil blast profile. An SP-6 commercial blast may be sufficient for many repair or DTM applications with less severe requirements. This coating is very tolerant of poor surface preparation; for tightly adhering existing coatings, degreasing and hand tool cleaning, power washing, brush blasting, sanding, or a combination of these methods may be acceptable. All surfaces to be coated must be clean, dry, and free of oil and grease, loose rust and paint, weld spatter,		burning slag, dust, and chalk. MIXING INSTRUCTIONS Mix 4 parts by volume #16-13057-FDA with 1 part 16-FDA Hardener. Mix at slow speed to avoid entraining air into the paint. Do not reuse previously used mixing containers; partially cured material will greatly accelerate the cure of the freshly mixed paint resulting in dramatically reduced pot life. THINNING Thin if necessary for spraying with xylol (or Acetone to maintain VOC). Add a little solvent at a time to the mixed system with constant gentle agitation to a maximum of 5% by volume. APPLICATION EQUIPMENT May be applied by air-assisted or airless spray. Airless spray gives the best results, use .015-.020 inch tip size. Apply 5.5 to 7.5 mils wet film thickness to yield 3-4 mils dry film thickness. Brushes should be of polyester or nylon construction if used. CURE TIMES & TEMPERATURES Cures set-to-touch in 1 hours at 77 ^0F, approximately 2 hours at 70 ^0F. If thicker films are desired retopcoat within 8-48 hours or reduced adhesion of the second coat may result. Allow 7-10 days cure at 70 ^0F before placing into severe service, longer if ambient temperature is lower.	CLEANUP Clean equipment with xylol or toluol before the film cures. ENVIRONMENTAL This product meets current air pollution regulations regarding hydrocarbon and ozone reactive emissions. It is VOC compliant for the architectural maintenance industry, and contains no lead, chromate, or zinc. PHYSICAL PARAMETERS VOC, ASTM D-3960: 3.10lb/gal mixed system WEIGHT PER GALLON, ASTM D-1475: 9.7lbs mixed system NONVOLATILE, mixed system: By weight: 68.0/- 2.0 % By volume: 55.0 +/- 1.0% THEORETICAL COVERAGE: 884 ft^2/gallon/mil, dry film INITIAL GLOSS, 60^0, ASTM D-523: 75 min. VISCOSITY, mixed system, ASTM D-562: 63-70 Krebs Units POT LIFE, mixed in 5 gal lots: greater than 8 hrs @ 77 ^0F FLASH POINT, TAG CC: 61 ^0F
THIS INFORMATION RESULTS FROM TESTS CONDUCTED IN A LABORATORY UNDER LABORATORY CONDITIONS. DIFFERENT RESULTS MAY BE OBTAINED IN COMMERCIAL USE OF THIS PRODUCT UNDER FACTORY OR FIELD CONDITIONS. PRUETT-SCHAFFER MAKES NO WARRANTY CONCERNING THE SUITABILITY OF THIS PRODUCT FOR THE END USE CONTEMPLATED BY THE BUYER, EXCEPT THAT THE PRODUCT SHALL BE IN COMPLIANCE WITH THE TECHNICAL SPECIFICATIONS PRESENTED HEREIN.

REVISED 03-25-2004