www.pruett-schaffer.com

PRODUCT NUMBER	PRODUCT NAME
13-4	LIGHT GRAY FAST DRY GLOSS EPOXY

GENERAL DESCRIPTION Pruett-Schaffer’s #13-4 Gray Epoxy is a two component, polyamidoamine –cycloaliphaticamine cured epoxy for use as a heavy duty maintenance top coat. It is designed as a gloss, brush or spray applied, corrosion resistant, ferrous metal coating. It exhibits excellent adhesion over a wide variety of substrates, and exceptional corrosion and chemical resistance. RECOMMENDED USES Use to protect machinery, tanks, and structures from corrosion in aggressive environments where chemicals, salt, water, fuels, and oils are present. Formulated to allow high film build in one pass to protect hard to cover sharp edges. Suitable for topcoating with a wide variety of epoxy, urethane, vinyl, or acrylic emulsion topcoats. May also be used as an encapsulation coating. This epoxy will chalk, topcoating is necessary for long term weathering exposure. SURFACE PREPARATION For severe service, metal substrates should be blasted to an SSPC-SP-10 white metal blast with a 1.5 +/- .5 mil blast profile. An SP-6 commercial blast may be sufficient for many repair or DTM applications with less severe requirements. This coating is very tolerant of poor surface preparation; for tightly adhering existing coatings, degreasing and hand tool cleaning, power washing, brush blasting, sanding, or a combination	of these methods may be acceptable. All surfaces to be coated must be clean, dry and free of oil and grease, loose rust and paint, weld spatter, burning slag, dust, and chalk. MIXING INSTRUCTIONS Mix 4 parts by volume #13-5-A with 1 part 13-B Hardener. Mix at slow speed to avoid entraining air into the paint. Use at once, there is no induction time. THINNING Thin if necessary for spraying with xylol or toluol. Add a little solvent at a time to the mixed system with constant gentle agitation to a maximum of 5% by volume. APPLICATION EQUIPMENT May be applied by air assisted or airless spray. Airless spray gives the best results, use .015-.020 inch tip size. Apply 4.5-7 mils wet film thickness to yield 3-5 mils dry film thickness. Application with a cup type spray gun is not recommended. CURE TIMES & TEMPERATURES Cures set-to-touch in 1-1.5 hours at 77 ^0F, and dry to handle in 2-4 hours. Topcoat within 3-48 hours or reduced adhesion of the second coat may result. Allow 7-10 days cure at 70 ^0F before placing into severe service, longer if ambient temperature is lower. Recommended minimum application temperature is 40 ^0F. Below 40 ^0F use 13-W winter cure hardener.	13-W will cause yellowing in light colors! CLEANUP Clean equipment with xylol or toluol before the film cures. ENVIRONMENTAL This product meets current air pollution regulations regarding hydrocarbon and ozone reactive emissions. It is VOC compliant for the architectural maintenance industry, and contains no lead, chromate, or zinc. PHYSICAL PARAMETERS VOC, ASTM D-3960: 1.89 lb/gal mixed system WEIGHT PER GALLON, ASTM D-1475: 11.02 lbs mixed system NONVOLATILE, mixed system: By weight: 82.8 ± 2.0 % By volume: 72.7 ± 1.0% THEORETICAL COVERAGE: 1167 ft^2/gallon/mil, dry film INITIAL GLOSS, 60^0, ASTM D-523: 70-90 VISCOSITY, mixed system, ASTM D-562: 75-85 Krebs Units POT LIFE, mixed in 5 gal lots: 4-6 hrs @ 77 ^0F; 1-2 hrs @ 90 ^0F FLASH POINT, TAG CC: 48 ^0F
THIS INFORMATION RESULTS FROM TESTS CONDUCTED IN A LABORATORY UNDER LABORATORY CONDITIONS. DIFFERENT RESULTS MAY BE OBTAINED IN COMMERCIAL USE OF THIS PRODUCT UNDER FACTORY OR FIELD CONDITIONS. PRUETT-SCHAFFER MAKES NO WARRANTY CONCERNING THE SUITABILITY OF THIS PRODUCT FOR THE END USE CONTEMPLATED BY THE BUYER, EXCEPT THAT THE PRODUCT SHALL BE IN COMPLIANCE WITH THE TECHNICAL SPECIFICATIONS PRESENTED HEREIN.

REVISED 06-06-2005